Mahendra Kumar Trivedi, Rama Mohan Tallapragada, Dahryn Trivedi, Gopal Nayak, Rakesh Kumar Mishra, Snehasis Jana

Neopentyl glycol (NPG) has been extensively used as solid-solid phase change materials (PCMs) for thermal energy storage applications. The objective of the present study was to evaluate the impact of biofield treatment on physical, spectral and thermal properties of NPG. The study was performed in two groups (control and treated). The control group remained as untreated, and treatment group was subjected to Mr. Trivedi’s biofield treatment. The control and treated NPG were characterized by X-ray diffraction (XRD), differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), and Fourier transform infrared (FT-IR) spectroscopy. XRD study revealed the decrease in crystallite size of treated NPG by 21.97% as compared to control sample. DSC studies showed slight change in melting temperature of treated NPG as compared to control sample. TGA analysis showed 55.66% weight loss in control NPG however, the treated sample showed reduction in weight loss (44.81%). Additionally, the maximum thermal decomposition temperature (Tmax) of treated NPG (160.40°C) was minimally increased with respect to control sample (159.72°C). This can be inferred as good thermal stability of biofield treated NPG with respect to control. FT-IR spectroscopy showed no structural changes in treated NPG with respect to control sample. The overall results showed that biofield treatment has affected the physical and thermal properties of treated NPG. Moreover, good thermal stability of treated NPG showed that it could be used as phase change materials for thermal energy storage applications.

Mahendra Kumar Trivedi, Dahryn Trivedi, Gopal Nayak, Ragini Singh, Snehasis Jana

P-Hydroxyacetophenone (pHAP) is an aromatic ketone derivative that is mainly used in the manufacturing of various pharmaceuticals, flavours, fragrances, etc. In the present study, the impact of Mr. Trivedi’s biofield energy treatment was analysed on various properties of pHAP viz. crystallite size, surface area, melting temperature, thermal decomposition, and spectral properties. The pHAP sample was divided into two parts; one was kept as control sample while another part was named as treated sample. The treated sample was given the biofield energy treatment and various parameters were analysed as compared to the control sample by X-ray diffraction (XRD), surface area analyser, thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), ultraviolet-visible (UV-VIS), and Fourier transform infrared (FT-IR) spectroscopy. The XRD studies showed the decrease in crystallite size of the treated sample (61.25 nm) as compared to the control (84.18 nm); however the intensity of peaks in diffractogram was increased in treated sample. Besides, the surface area of treated sample was decreased by 41.17% as compared to the control. The TGA analysis revealed that onset temperature as well as Tmax (maximum thermal decomposition temperature) was increased in the treated sample. However, the latent heat of fusion (ΔH) was decreased from 124.56 J/g (control) to 103.24 J/g in the treated sample. The treated and control samples were also evaluated by UV-Vis and FT-IR spectroscopy and did not show any significant alteration in spectra of treated sample as compared to the respective control. Hence, the overall results suggest that there was an impact of biofield energy treatment on the physical and thermal properties of pHAP sample.

Mahendra Kumar Trivedi, Dahryn Trivedi, Gopal Nayak, Gunin Saikia, Snehasis Jana

Benzene, toluene and p-xylene are derivatives of benzene, generally produced from crude petroleum and have numerous applications in industry. The aim of the present study was to evaluate the impact of biofield treatment on isotopic abundance of these benzene derivatives by gas chromatography-mass spectrometry (GC-MS). Benzene, toluene and p-xylene samples were divided into two parts: control and treatment. Control part was remained as untreated and treatment part was subjected to Mr. Trivedi’s biofield treatment. Control and treated samples were characterized using GC-MS. GC-MS data revealed that isotopic abundance ratio of 13C/12C or 2H/1H (PM+1/PM) of treated samples were significantly increased from un-substituted to substituted benzene rings (where, PM- primary molecule, PM+1- isotopic molecule either for 13C/12C and/or 2H/1H). The isotopic abundance ratio of 13C/12C or 2H/1H (PM+1/PM) in benzene was decreased significantly by 42.14% as compared to control. However, the isotopic abundance ratio of (PM+1/PM) in treated toluene and p-xylene was significantly increased up to 531.61% and 134.34% respectively as compared to their respective control. Thus, overall data suggest that biofield treatment has significantly altered the isotopic abundance ratio of (PM+1/PM) in a different way for un-substituted and substituted benzenes.

Mahendra Kumar Trivedi, Dahryn Trivedi, Gopal Nayak, Khemraj Bairwa, Snehasis Jana

The p-anisidine is widely used as chemical intermediate in the production of various dyes, pigments, and pharmaceuticals. This study was aimed to evaluate the effect of biofield energy treatment on the physicochemical and spectroscopic properties of p-anisidine. The study was performed after dividing the sample in two groups; one was remained as untreated and another was subjected to Mr. Trivedi’s biofield energy treatment. Afterward, both the control and treated samples of p-anisidine were evaluated using X-ray diffraction (XRD), surface area analyzer, differential scanning calorimetry (DSC), thermogravimetric analysis-derivative thermogravimetry (TGA-DTG), Fourier transform infrared (FT-IR), and ultraviolet-visible (UV-Vis) spectroscopy. The XRD analysis showed the increase in unit cell volume from 683.81 → 690.18 × 10-24 cm3 and crystallite size from 83.84→84.62 nm in the treated sample with respect to the control. The surface area analysis exhibited the significant increase (25.44%) in the surface area of treated sample as compared to control. The DSC thermogram of control p-anisidine showed the latent heat of fusion and melting temperature and 146.78 J/g and 59.41°C, respectively, which were slightly increased to 148.89 J/g and 59.49°C, respectively after biofield treatment. The TGA analysis showed the onset temperature of thermal degradation at 134.68°C in the control sample that was increased to 150.02°C after biofield treatment. The result showed about 11.39% increase in onset temperature of thermal degradation of treated p-anisidine as compared to the control. Moreover, the Tmax (temperature at which maximum thermal degradation occurs) was also increased slightly from 165.99°C (control) to 168.10°C (treated). This indicated the high thermal stability of treated p-anisidine as compared to the control. However, the FT-IR and UV spectroscopic studies did not show any significant changes in the spectral properties of treated p-anisidine with respect to the control. All together, the XRD, surface area and thermal analysis suggest that Mr. Trivedi’s biofield energy treatment has the impact on physical and thermal properties of the treated p-anisidine.